Zinc-It is a locally manufactured cold galvanizing compound. When Zinc-it is applied to properly prepared steel, it prolongs the useful life by as much as three (3) times, compared to traditional red oxide coating.
Zinc-It is widely used for coating the following:
Strututral Steel Members
Galvanize and Aluzinc Roof Sheeting
Wrougt Iron Works
Under Body of Vehicles
Appliances such as Washing Machines, Dryers, Refrigerators, Freezers, Stoves etc.
Zinc-It also affords the following:
Industrial strength protection against corrosion
Prevent moisture from penetrating and rust developing.
Outlasts traditional red oxide products by as much as three (3) times longer
Resistant to abrasion
Withstands temperatures up to 350oF
Ready to use, straight out of the can
Surface preparation: Light Duty – Wire Brushing Severe Duty – Abrasive Blasting
Zinc-It is a superior product that will provide longer lasting protection against corrosion.
This product is not recommended for:
Contact with potable water
Strong acids or Strong alkalis
Weight per US Gallon |
- |
17 lbs |
|
Coverage @ 1.5 mils |
- |
260 sq. ft/gal |
|
Zinc Content |
- |
97% in dry film |
|
Solids by Volume |
- |
80% |
|
Consistency |
- |
Slightly Thixotripic, needs to be stirred. |
|
Touch Dry |
- |
1.5 - 3 min |
|
Curing Time |
- |
25 - 35 min |
|
Re-coat Time |
- |
25 - 35 min |
|
Shelf-Life |
- |
Almost Unlimited |
|
Flash Point |
- |
1400 F |
|
Toxicity |
- |
Non-Toxic |
|
Recommended Solvent |
- |
Zinc-It R5 |
|
Wet Mils |
- |
3.5 - 6.0 |
|
Dry mils |
- |
2.0 - 3.5 |
|
Surface Prep (long life) |
- |
Commercial blast( 10 + years) |
|
Surface Prep (short life) |
- |
Remove Loose Rust ( 5 years) |
|
Top-Coating |
- |
Compatible with Several Top Coats |
|
Temperature Limit |
- |
9000 F |
|
|
|
|
|
DIRECTIONS FOR USE
|
|||